PA6G - cast polyamide 6

Other material names PA6G: silon, nylon

Material group:

Polyamide

Cast nylon polyamides, commonly called nylon type PA6G, or PA6 C are manufactured in standard stock shapes and cast in the form of sheet, rod and tube. Cast nylon polyamides are highly molecular, highly crystalline polymers. Semi finished nylon type 6 shapes are manufactured using a casting method, whereby the raw material caprolactam polymerises by means of a controlled chemical reaction.

By using additives such as oil, solid lubricants or thermal stabilisers, the typical characteristics of type 6 nylon can be selectively adjusted for certain applications, opening up a custom tailored range of materials to cover a wide application spectrum. Cast Nylon demonstrates even higher crystallinity and better machinability than extruded nylon.

Color of material:

Natur

Black

Delivery of this material is also possible in other colors - for example blue, red, green, yellow ... These colors are not in stock and their delivery is possible only after previous demand.

Typical applications:

Rollers
Slide bearings
Slide elements
Components under varying stress
Parts subject to high impacts and shocks

Show more our products

Our products made of material PA6G

The material is used in:

Electrotechnical industry

Automobile industry

Packaging industry

Engineering industry

Steel industry

Construction machines

Production of single-purpose machines

Features:

Very low levels of internal stress
High degree of crystallinity
Toughness at high levels of hardness
Very good wear resistance
Good abrasion resistance
Good damping properties
Easy processing
Ability to be manufactured in wide ranging casting weights and dimensions

Material availability:

Material is in stock

Group of materials Polyamide:

Comparison of material properties

Comparison of material properties from the group Polyamide

	PA6G+oil	PA6G+MoS2	PA6G	PA66+GF30	PA66	PA6	PA4.6	PA12G
Specific weight	1.14 g/cm³	1.16 g/cm³	1.15 g/cm³	1.29 g/cm³	1.14 g/cm³	1.14 g/cm³	1.18 g/cm³	1.03 g/cm³
Yield strength	80 N/mm²	78 N/mm²	85 N/mm²	160 N/mm²	85 N/mm²	76 N/mm²	100 N/mm²	60 N/mm²
Tensile strength
Allowable mean pressure deformation 1%	22.00 N/mm²	25.00 N/mm²	26.00 N/mm²	28.00 N/mm²	25.00 N/mm²	24.00 N/mm²	23.00 N/mm²
Allowable mean pressure deformation 2%	43.00 N/mm²	49.00 N/mm²	51.00 N/mm²	55.00 N/mm²	49.00 N/mm²	46.00 N/mm²	45.00 N/mm²
Allowable mean pressure deformation 5%	79.00 N/mm²	88.00 N/mm²	92.00 N/mm²	90.00 N/mm²	90.00 N/mm²	80.00 N/mm²	94.00 N/mm²
p.v dry limit	0.23 MPa.m/s		0.13 MPa.m/s		0.13 MPa.m/s	0.11 MPa.m/s		0.10 MPa.m/s
Flexural strength	140 N/mm²		140 N/mm²	250 N/mm²	135 N/mm²	130 N/mm²	150 N/mm²	90 N/mm²
Tensibility	50 %	25 %	40 %	5 %	50 %	50 %	25 %	55 %
Flexural modulus	2 800 N/mm²		3 200 N/mm²		2 900 N/mm²	2 500 N/mm²	3 200 N/mm²	1 500 N/mm²
Tensile modulus	2 600 N/mm²	3 300 N/mm²	3 500 N/mm²	11 000 N/mm²	3 000 N/mm²	3 200 N/mm²	3 300 N/mm²	2 000 N/mm²
Impact toughness	bez zlomu	bez zlomu	bez zlomu	50	bez zlomu	bez zlomu	bez zlomu	bez zlomu
Notched toughness	>5 kJ/m²	>3 kJ/m²	>4 kJ/m²	>6 kJ/m²	>4 kJ/m²	>5 kJ/m²	>8 kJ/m²	>15 kJ/m²
Ball hardness	140 N/mm²	160 N/mm²	165 N/mm²	240 N/mm²	170 N/mm²	150 N/mm²	165 N/mm²	100 N/mm²
Friction coefficient	0.18	0.32	0.35	0.45	0.35	0.38	0.35	0.32
Sliding wear	0.05 um/km	0.10 um/km	0.10 um/km		0.10 um/km	0.23 um/km		0.80 um/km
Abrasive wear			150		160			260
Antistatic material	No	No	No	No	No	No	No	No
Permittivity	3.70	3.60	3.60	3.90	3.80	3.90	3.80	3.50
Electrical strength	22 kV/mm	24 kV/mm	25 kV/mm	30 kV/mm	27 kV/mm	25 kV/mm	25 kV/mm	20 kV/mm
Specific internal resistance	10^(14) Ω	10^(13) Ω	10^(13) Ω	10^(14) Ω	10^(12) Ω	10^(12) Ω	10^(14) Ω	10^(14) Ω
Specific surface resistance	10^(13) Ω.cm	10^(12) Ω.cm	10^(12) Ω.cm	10^(13) Ω.cm	10^(12) Ω.cm	10^(12) Ω.cm	10^(13) Ω.cm	10^(13) Ω.cm
Melting point	220 °C	220 °C	220 °C	255 °C	265 °C	220 °C	295 °C	179 °C
Thermal expansion	8 10^(-5)/K	8 10^(-5)/K	8 10^(-5)/K	3 10^(-5)/K	10 10^(-5)/K	10 10^(-5)/K	9 10^(-5)/K	10 10^(-5)/K
Thermal conductivity	0.23 W/(K.m)	0.30 W/(K.m)	0.29 W/(K.m)	0.30 W/(K.m)	0.28 W/(K.m)	0.28 W/(K.m)	0.30 W/(K.m)	0.23 W/(K.m)
Permanent use temperature	-40-105	-30-105	-40-105	-30-120	-30-100	-30-95	-40-155	-60-80
Transient temperature of use	-40-160	-40-170	-40-170	-30-180	-30-150	-40-140	-40-200	-60-140
Friction coefficient	0.18	0.32	0.35	0.45	0.35	0.38	0.35	0.32
Absorbability	1,8 %	2,4 %	2.2 %	1,7 %	2,5 %	2,6 %	2,8 %	0,9 %
Water absorption	5,5 %	6,7 %	6.5 %	5,5 %	9 %	10 %	9,5 %	1,4 %
Resistance - oils	resistant	resistant	resistant	resistant	resistant	resistant	resistant	resistant
Acid resistance	conditionally resistant	conditionally resistant	conditionally resistant	conditionally resistant	conditionally resistant	conditionally resistant	conditionally resistant	conditionally resistant
Durability - alcali	resistant	resistant	resistant	resistant	conditionally resistant	conditionally resistant	conditionally resistant	resistant
Food contact	No	No	No	No	No	No	No	No
Special features	samomazné vlastnosti					PA6 can absorb up to 7% (by weight) water under high humidity or submerged in water. This can result in dimensional changes up to 2% and a corresponding reduction of physical properties. Proper design techniques can frequently compensate for this factor.	Highest heat resistance of PA materials

Material properties table

Specific weight	1.15 g/cm³
Yield strength	85 N/mm²
Allowable mean pressure deformation 1%	26.00 N/mm²
Allowable mean pressure deformation 2%	51.00 N/mm²
Allowable mean pressure deformation 5%	92.00 N/mm²
p.v dry limit	0.13 MPa.m/s
Flexural strength	140 N/mm²
Tensibility	40 %
Flexural modulus	3 200 N/mm²
Tensile modulus	3 500 N/mm²
Impact toughness	bez zlomu
Notched toughness	>4 kJ/m²
Ball hardness	165 N/mm²
Friction coefficient	0.35
Sliding wear	0.10 um/km
Abrasive wear	150
Antistatic material	No
Permittivity	3.60
Electrical strength	25 kV/mm
Specific internal resistance	10^(13) Ω
Specific surface resistance	10^(12) Ω.cm
Melting point	220 °C
Thermal expansion	8 10^(-5)/K
Thermal conductivity	0.29 W/(K.m)
Permanent use temperature	-40 ; 105 °C
Transient temperature of use	-40 ; 170 °C
Absorbability	2.2 %
Water absorption	6.5 %
Resistance - oils	resistant
Acid resistance	conditionally resistant
Durability - alcali	resistant
Food contact	No

Some trade names of the material

Tecast®

Murylon® 6 G

Ertalon® 6 PLA

Zellamid® 1100

Trade names unprotected reg. mark:

silon, nylon

Engineering plastics and their products can be ordered from TechPlasty. Materials in the same group from different manufacturers are not always directly interchangeable because they may not all have the same technical parameters. Our technical consultants, who have many years of experience in the field of engineering plastics, will be pleased to advise you on the differences in the individual materials, especially in the boundary conditions. Detailed technical data of individual manufacturers' materials can be found in their data sheets.

Some materials trade names are protected trademarks..
Tecast® is a registered trademark of Ensinger; Murylon® 6 G sis a registered trademark of Murtfeldt; Ertalon® 6 PLA is a registered trademark of Quadrant; Zellamid® 1100 is a registered trademark of Zell-Metall;

All other trademarks or registered trademarks are the property of their respective owners.

Content for comparison

PA6G - cast polyamide 6

Our offer

The most used plastics

TechPlasty

Quick contact

You are here

Content for comparison

PA6G - cast polyamide 6

Our offer

The most used plastics

TechPlasty

Quick contact